600g Fibreglass Woven Roving Plain Woven Cloth

 

600g Fibreglass Woven Roving Plain Woven Cloth

 

 

1.______________/ Description of Fiberglass Woven Roving :

 

Glass woven rovings are bidirectional fabric made by direct rovings in plain weave pattern.

Compatible with unsaturated polyester,vinyl resin,epoxy resin.

Applicable for hand lay-up,winding and compress molding process,suitable for manufacturing tank,boat,antomobile parts and other FRP products.

 

Reinforced Fiberglass Cloth is made of high strength E glass fiberglass yarn, with plain or twill weaving style. It is widely used in aircraft and spaceflight industry, ship industry, chemical industry, medical industry, military industry and sports goods, etc. It can be used to produce golf pole, surfboard, sailboard, boat hull, FRP tank, swimming pools, car bodies, FRP pipe as well as other FRP products.

 

 

600g E-glass Fiberglass Woven Roving is a woven material available in various sizes to allow custom strength, thickness, and weight in projects. Fiberglass cloth provides great strength and durability when layered with a resin to form a hardened composite.

 

Explain For EWR 600-100:

                                            ____Width(cm)

                                ____Mass(g/m2)

  ____Product Type:

                                EWR:E-GLASS WOVEN ROVING

                                CWR:C-GLASS WOVEN ROVING

 

 

2._____________________/Specification Of Fiberglass Woven Roving:

 

Style	Yarn(tex)	Density(ends/10cm)		Mass(g/m2)	Width(cm)	Tensile Strength(N/50mm)
		Warp	Weft			Warp	Weft
EWR200	200	50	50	200±16	90/100	≥1300	≥1100
EWR400	600	35	32	400±32	100/127	≥2500	≥2200
EWR570	1150	26	24	570±45	100/127	≥3600	≥3300
EWR600	1200	26	24	600±48	100/127	≥4000	≥3850
EWR800	2400	18	16	800±64	100/127	≥4600	≥4400
CWR400	500	40	40	400±32	90/100	≥2000	≥1900
CWR600	1200	26	24	600±48	100/127	≥2750	≥2600
CWR800	2400	18	16	800±64	100/127	≥3000	≥2900

 

 

 

3.______________________/Feature Of Fiberglass Woven Roving:

• Consistent thickness and excellent surface treatment.
• Rapid impregnating and good compatibility with resin
• Uniform tension,high dimensional stability and making handing easy
• Good mechanical properties  and high strength of parts

 

4.______________________/Packaging and Storage

 

1. Each roll is packed by polyester bag,and then put into a cardboard box or plastic woven bag.
2. The weight is each roll is between 20—85kg.
3. The rolls are to be horizontally placed and could be in bulk or on pallet,
4. Optimum storage conditions are between the temperature of 5—35℃,humidity between 35%—65%.
5. The products should be used within 12 months from the time of delivery and remain in theiroriginal packaging until just prior to use.

 

 